Non-doped Single Mode Fiber
|
|
|
Item
|
NA
|
Core dia.
|
Cladding dia.
|
Coating dia.
|
Cut-off
|
Loss
|
-
|
µm
|
µm
|
µm
|
nm
|
dB/m@nm
|
ZSF-6/125-N-0.20
|
0.20±0.01
|
6±1
|
123±3
|
460±30
|
<1850
|
<0.1@1500
|
ZSF-6/125-N-0.26
|
0.26±0.01
|
6±1
|
123±3
|
460±30
|
<2400
|
<0.1@1500
|
|
0.20±0.01
|
9±1
|
123±3
|
460±30
|
<2600
|
<0.1@1500
|
ZSF-9/125-N-0.26
|
0.26±0.01
|
9±1
|
123±3
|
460±30
|
<3950
|
<0.1@1500
|
|
|
|
|
|
|
Non-doped Multi Mode Fibers
|
|
|
Item
|
NA
|
Core dia.
|
Cladding dia.
|
Coating dia.
|
Loss
|
µm
|
µm
|
µm
|
dB/m@nm
|
|
0.29±0.01
|
95±5
|
123±5
|
460±30
|
<0.1@2500
|
|
0.29±0.01
|
160±10
|
200±10
|
480±30
|
<0.1@2500
|
|
0.29±0.01
|
400±25
|
500±25
|
600±30
|
<0.1@2500
|
|
|
|
|
|
|
Double Cladding Fibers
|
|
|
Item
|
Dopant
|
Concentration
|
Core dia.
|
1st Cladding
configuration
|
2nd Cladding dia.
|
Loss Spectrum
|
ppm mol
|
µm
|
µm
|
µm
|
|
|
60,000
|
18±3
|
250/Circular
|
400±30
|
-
|
|
|
60,000
|
30±3
|
300/Circular
|
460±30
|
-
|
|
|
40,000
|
7.5±1.
|
120/Circular
|
210±20
|
-
|
|
|
2,000/40,000
|
8.5±1.5
|
123/Cicular
|
210±20
|
-
|
|
|
|
|
|
|
◇Current Stock
|
|
|
Single Mode Fibers
|
|
|
Item
|
Dopant
|
Concentration
|
NA
|
Core dia.
|
Cladding dia.
|
Coating dia.
|
Cut-off
|
Loss Spectrum
|
ppm mol
|
-
|
µm
|
µm
|
µm
|
nm
|
|
non
|
-
|
0.18
|
9±1
|
123±3
|
450±30
|
<2350
|
|
|
Tm
|
3,200
|
0.26
|
2.7±0.3
|
123±3
|
450±30
|
<1050
|
|
ZSF-9/125-13T
|
Tm
|
13,000
|
0.16
|
8.5±1.5
|
125±3
|
450±30
|
<2200
|
|
|
Pr
|
1,500
|
0.25
|
2.4±0.4
|
123±3
|
450±30
|
<950
|
|
|
Er
|
2,000
|
0.21
|
4.7±0.5
|
123±3
|
450±30
|
<1450
|
-
|
|
Er
|
5,000
|
0.12
|
5.5±0.5
|
123±3
|
450±30
|
<950
|
|
|
Ho
|
1,000
|
0.16
|
9.0±1.0
|
123±3
|
450±30
|
<2100
|
|
|
Ce
|
40,000
|
0.12
|
13.0±2.0
|
123±3
|
450±30
|
<2350
|
|
|
|
|
|
|
|
PM (ellipsoidal core)-Single Mode Fibers
|
|
|
Item
|
Dopant
|
Concentration
|
Extinction ratio
|
Core dia.
|
Cladding dia.
|
Coating dia.
|
Cut-off
|
Loss Spectrum
|
ppm mol
|
dB
|
µm
|
µm
|
µm
|
nm
|
ZSF-2.2x5.5/125-N-PM
|
|
-
|
>20@1.3μm
|
2.2x5.5
|
123±3
|
450±30
|
<1300
|
|
|
|
|
|
|
|
Multi Mode Fibers
|
|
|
Item
|
Dopant
|
Concentration
|
NA
|
Core dia.
|
Cladding dia.
|
Coating dia.
|
Loss Spectrum
|
ppm mol
|
µm
|
µm
|
µm
|
|
non
|
-
|
0.27±0.01
|
90±5
|
123±6
|
480±30
|
|
|
non
|
-
|
0.27±0.01
|
395±35
|
500±25
|
600±30
|
|
|
|
|
|
|
|
Double Cladding Fibers
|
|
|
Item
|
Dopant
|
Concentration
|
Core dia.
|
1st Cladding
configuration
|
2nd Cladding dia.
|
Loss Spectrum
|
ppm mol
|
µm
|
µm
|
µm
|
|
|
60,000
|
70±11
|
250/Circular
|
400±10
|
|
|
|
5,000
|
4.7±0.7
|
124/Cicular
|
200±10
|
|
ZDF-7.5/125-20T-C
|
Tm
|
20,000
|
7.5±1.5
|
120/Circular
|
215±10
|
|
ZDF-7.5/125-30T-C
|
Tm
|
30,000
|
7.5±1.5
|
120/Circular
|
215±10
|
|
ZDF-7.5/125-35T-C
|
Tm
|
35,000
|
7.5±1.5
|
120/Circular
|
215±10
|
|
|
|
20,000
|
10±1
|
124/Circular
|
200±10
|
|
ZDF-10/125-30H2.5P-O
|
Ho/Pr
|
30,000/2,500
|
10±1
|
125/Octagonal
|
185±15
|
click here
|
|
|
13,000
|
4.5±0.5
|
123/Circular
|
217±30
|
|
|
|
33,700
|
3±0.6
|
123/Circular
|
200±10
|
|
|
|
|
Note: 2nd cladding is flurorine-contained resin.
|
|
|
|
|
|
■ AlF3 based Fibers & Cable
|
|
|
|
|
|
|
|
|
Non-doped Multi Mode Fibers
|
|
|
Item
|
NA
|
Core dia.
|
Cladding dia.
|
Coating dia.
|
Loss
|
µm
|
| |